MAJORIS DM400 - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ql3eu9_MAJORIS-DM400---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DM400 - 8229 is a 40% mica reinforced polypropylene compound intended for injection moulding. APPLICATIONS Products requiring high rigidity, heat resistance, low shrinkage, high dimensional stability can suitably be made from DM400 - 8229. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 - 0.80 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 38.0 | MPa | ISO 527-2/5 |
| Fracture | 35.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 1.3 | % | ISO 527-2/5 |
| Fracture | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 5950 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 101 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 270 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP QR673K | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| NORYL™ HM4025H resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| Durepol® PBT A3 G30 NTLA010 BT302 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| Ekalon® 20 E I S F | Sattler KunststoffWerk GmbH | PC | Ekalon® |
| LEXAN™ IR2040 resin | SABIC Innovative Plastics | PC | LEXAN™ |