Sarlink® TPE AB-1238DN
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qiYkE4_Sarlink-TPE-AB-1238DN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE AB-1238DN is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Sarlink®The typical application field of TPE AB-1238DN is: automobile industry |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ISO 2577 | ||
| Flow | 1.2 | % | ISO 2577 |
| Transverse flow | 1.2 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.023 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 8.0E-3 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 10 sec) | 44 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| 23°C | 138 | MPa | ISO 527-2 |
| 85°C | 12.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, -35°C | 25.6 | MPa | ISO 527-2 |
| Fracture, 23°C | 21.7 | MPa | ISO 527-2 |
| Fracture, 85°C | 5.50 | MPa | ISO 527-2 |
| 100% strain, -35 c | 16.5 | MPa | ISO 527-2 |
| 100% strain, 23°C | 8.41 | MPa | ISO 527-2 |
| 100% strain, 85°C | 4.30 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Fracture, -35°C | 480 | % | ISO 527-2 |
| Fracture, 23°C | 690 | % | ISO 527-2 |
| Fracture, 85°C | > 500 | % | ISO 527-2 |
| Flexural Modulus | ISO 178 | ||
| 23°C | 205 | MPa | ISO 178 |
| 85°C | 34.3 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| -35°C | 130 | kN/m | ISO 34-1 |
| 23°C | 74 | kN/m | ISO 34-1 |
| 85°C | 40 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Annealed) | 43.9 | °C | ISO 75-2/B |
| Glass Transition Temperature | -60.0 | °C | DSC |
| Melting Temperature (DSC) | 159 | °C | ISO 3146 |
| Additional Information |
|---|
| 火灾水平蔓延速率= 3.3 英寸/分钟(83 毫米/分钟)雾化，3小时，100 C箱内展开 (-35C) = 合格 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBE Nylon 5021 T | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| Dynacom CL6153 | Dynachem Co. Ltd. | PP Copolymer | Dynacom |
| KOPELEN J-340C | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| KMI KM12SAC | KMI Group, Inc. | Acrylic (SMMA) | KMI |
| Hostacom PPU X9067HS 151237 | LyondellBasell Industries | PP Copolymer | Hostacom |