Ferro PP LPP20BN03HB-BK
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qiDlSb_Ferro-PP-LPP20BN03HB-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ferro PP LPP20BN03HB-BK is a Polypropylene Copolymer (PP Copolymer) material filled with 21% calcium carbonate. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Ferro PP LPP20BN03HB-BK are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.6 | % | |
| Across Flow | 1.7 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 71 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 23.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 60 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : 23°C | 1530 | MPa | |
| Tangent : 23°C | 1690 | MPa | |
| Flexural Strength (23°C) | 37.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D4812 |
| Gardner Impact (23°C) | 16.4 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 101 | °C | |
| 1.8 MPa, Unannealed | 57.2 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 202 to 204 | °C | |
| Middle Temperature | 204 to 210 | °C | |
| Front Temperature | 210 to 213 | °C | |
| Nozzle Temperature | 213 to 218 | °C | |
| Mold Temperature | 43.3 to 51.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 3067-85A-0000 | Vi-Chem Corporation | TPE | Sevrene® |
| Styrolution PS 486N | INEOS Styrolution Group GmbH | PS (HIPS) | Styrolution PS |
| NOVALAC FM 7700 | Vyncolit N.V. | Phenolic | NOVALAC |
| Cheng Yu FR200GV10 | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| KPOL-PP K-PPH 2.1 S | KPOL Chem Co. | PP Homopolymer | KPOL-PP |