Hostacom EYC 772N
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qhZAUv_Hostacom-EYC-772N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom EYC 772N very high melt flow, mineral-filled polypropylene copolymer has a good balance of properties and processability. It was designed primarily for automotive interior applications that require high rigidity and good scratch and mar resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792A, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 25.0 | MPa | ASTM D638 |
| Yield | 25.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.5 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2 |
| Break 2 | 18 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 2500 | MPa | ASTM D790 |
| -- | 2300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 7.0 | kJ/m² | ISO 180 |
| Gardner Impact | 12.5 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 108 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 112 | °C | ISO 75-2/B |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBW108LE | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| XYRON™ 640V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| FINGERPRINT™ DFDA-7510 NT | The Dow Chemical Company | LLDPE | FINGERPRINT™ |
| Globalene® PH5201 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| LEXAN™ FXD1414T resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |