PREPERM® L700HF
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | Premix Oy |
| Trademark: | PREPERM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qh2dAB_PREPERM-L700HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PREPERM® L700HF is a special compound with elevated dielectric constants of 7.0. PREPERM® L700HF is a special compound based on Premix proprietary PPE technology. Extremely low dissipation factor (< 0.001) makes PREPERM® L700HF an excellent material for high frequency applications. PREPERM® L700HF offers stable dielectric constant over wide frequency and wide temperature range. PREPERM® L700HF is modified for injection moulding. Applications include structural parts for antennas in base stations, point to point, wlan, mobile phones etc. Devices made out of PREPERM® can operate at very high frequencies as PREPERM® offers stable performance even at 120 GHz. |
| General Information | |
|---|---|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.98 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (4.00 mm) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 5.0 | % | ISO 527-2 |
| Flexural Modulus (4.00 mm) | 4500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | ISO 180 | ||
| -20°C | 4.0 | kJ/m² | ISO 180 |
| 23°C | 4.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength 2 | ISO 180 | ||
| -20°C | 30 | kJ/m² | ISO 180 |
| 23°C | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 140 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 122 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.00 GHz) | 7.00 | Internal method | |
| Dissipation Factor (1.00 GHz) | 6.0E-4 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 290 - 310 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Injection Pressure: High |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Boda BDF-LG2701 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Hylon® N1213STHL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| ICORENE® K 4140 | ICO Polymers SA, A Division of A. Schulman | XLPE | ICORENE® |
| LNP™ LUBRICOMP™ WFL34 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |
| TOTAL Polystyrene Crystal 585B | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |