Cereplast Compostables® 7003
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Cereplast, Inc. |
| Trademark: | Cereplast Compostables® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qgvZNx_Cereplast-Compostables-7003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cereplast Compostables® resins are renewable, ecologically sound substitutes for petroleum-based plastic product replacing nearly 100% of the petroleum-based additives used in traditional plastics. Cereplast Compostables® resins are using polymer and additives derived from starch and other renewable resources chemistry. These components are carefully blended together on state-of-the-art compounding equipments. All Cereplast Compostables® resins, including Compostable 7003, are certified as biodegradable and compostable in the United States and Europe, meeting BPI (Biodegradable Products Institute www.bpiworld.com) standards for compostability (ASTM6400D99, ASTM6868) and European Bioplastics Standards (EN13432). Compostable 7003 has been designed to have an excellent balance of strength, toughness and processability. Compostable 7003 can be processed on existing sheet extrusion machines. Please see our processing guide for processing and material drying guidelines. This can be found at www.cereplast.com. Compostable 7003 is recommended for extrusion application like straws, profiles, boards, sheets, pipes, conduits, and more… |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength (Break) | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 33 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 50.0 | °C | ASTM D648 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Cylinder Zone 1 Temp. | 174 - 185 | °C | |
| Cylinder Zone 2 Temp. | 177 - 185 | °C | |
| Cylinder Zone 3 Temp. | 177 - 196 | °C | |
| Adapter Temperature | 177 - 196 | °C | |
| Melt Temperature | 199 | °C | |
| Die Temperature | 177 - 196 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 20 to100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Udel® P-1750 MR | Solvay Specialty Polymers | PSU | Udel® |
| ArgoGraph® 46510 WHITE | Argotec LLC | TPU, Unspecified | ArgoGraph® |
| Kazan LDPE 153 VSKM | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |
| Lucky Enpla LAY1003 | Lucky Enpla Co LTD | PC+ABS | Lucky Enpla |
| Parylene HT® | Specialty Coating Systems (SCS) | PPX | Parylene |