LNP™ THERMOTUF™ V1000SU compound
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qgoTYY_LNPTHERMOTUFV1000SUcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF V1000SU is a compound based on Nylon resin. Added features of this material include: Heat Stabilized, UV Stabilized. Also known as: LNP* THERMOTUF* Compound V-1000 HS UV Product reorder name: V1000SU |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 2.1 - 2.3 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.5 - 2.7 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 2.6 | % | ISO 294-4 |
| Flow direction : 24 hours | 2.2 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 1700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 55.2 | MPa | ASTM D790 |
| -- | 53.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D256 |
| 23°C 1 | 27 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 192 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 2 | 150 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 193 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 3 | 147 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.4E-4 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 1.3E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 260 - 271 | °C | |
| Middle Temperature | 271 - 282 | °C | |
| Front Temperature | 288 - 299 | °C | |
| Processing (Melt) Temp | 271 - 293 | °C | |
| Mold Temperature | 48.9 - 93.3 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 10 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 mm |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3893 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Shinko-Lac® ASA S411 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Adell Polyamide BJ-34 Glass Reinforced High Impact | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| ASTALON™ H4000 | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| Axiall PVC 4750 | Axiall Corporation | PVC, Flexible | Axiall PVC |