NANCAR® 3555J
| Category: | NBR , Acrylonitrile Butadiene Rubber |
| Manufacturer: | Nantex Industry Co., Ltd. |
| Trademark: | NANCAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qggtc0_NANCAR-3555J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NANCAR® 3555J is a medium high acrylonitrile butadiene copolymer with excellent oil resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. It has fast curing rate, low mold fouling and superior resilience properties. It has good processing characteristics in compounds where flow and knitting are desired and is especially valuable in high durometer compounds. NANCAR® 3555J provides good processing and building tack. It is suggested for use in molded goods, friction stock and similar applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.00 | g/cm³ | |
| Mooney Viscosity | ASTM D1646 | ||
| ML 1+4, 100°C 1 | 71 | MU | |
| ML 1+4, 100°C | 55 | MU | |
| Acrylonitrile Content - Bound | 35.0 | % | Internal Method |
| Solubility - in MEK | 100 | % | |
| Stabilizer | Non-staining | ||
| Viscosity | |||
| Minimum | 47.0 | ASTM D1646 | |
| Minutes to 35 points rise, t35 | 31.5 | min | |
| Minutes to 5 points rise, t5 | 22.3 | min |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Loss | 0.30 | % | ASTM D5688 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 5 sec 2 | 74 | ||
| Shore A, 5 sec 3 | 73 | ||
| Shore A, 5 sec 4 | 72 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 300% Strain 5 | 9.80 | MPa | |
| 300% Strain 6 | 8.90 | MPa | |
| 300% Strain 7 | 6.30 | MPa | |
| Tensile Strength | ASTM D412 | ||
| Yield 8 | 29.7 | MPa | |
| Yield 9 | 27.9 | MPa | |
| Yield 10 | 27.1 | MPa | |
| Tensile Elongation | ASTM D412 | ||
| Break 11 | 610 | % | |
| Break 12 | 640 | % | |
| Break 13 | 770 | % | |
| Tear Strength | 64.0 | kN/m | ASTM D624 |
| Compression Set 14(100°C, 70 hr) | 76 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 15(100°C, 70 hr) | -5.0 | % | ASTM D573 |
| Change in Ultimate Elongation in Air 16(100°C, 70 hr) | -39 | % | ASTM D573 |
| Change in Durometer Hardness in Air 17(Shore A, 100°C, 70 hr) | 6.0 | ASTM D573 | |
| Change in Tensile Strength 18 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | -6.0 | % | |
| 100°C, 70 hr, in IRM 903 Oil | -18 | % | |
| Change in Ultimate Elongation 19 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | -31 | % | |
| 100°C, 70 hr, in IRM 903 Oil | -28 | % | |
| Change in Durometer Hardness 20 | ASTM D471 | ||
| Shore A, 100°C, 70 hr, in ASTM #1 Oil | 4.0 | ||
| Shore A, 100°C, 70 hr, in IRM 903 Oil | -7.0 | ||
| Change in Volume 21 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM Oil #1 | -0.25 | % | |
| 100°C, 70 hr, in IRM 903 Oil | 12 | % |
| Note Message | |
|---|---|
| 1 . | Uncured |
| 2 . | CURED @150°C for 60 mins |
| 3 . | CURED @150°C for 40 mins |
| 4 . | CURED @150°C for 20 mins |
| 5 . | CURED @150°C for 60 mins |
| 6 . | CURED @150°C for 40 mins |
| 7 . | CURED @150°C for 20 mins |
| 8 . | CURED @150°C for 60 mins |
| 9 . | CURED @150°C for 40 mins |
| 10 . | CURED @150°C for 20 mins |
| 11 . | CURED @150°C for 60 mins |
| 12 . | CURED @150°C for 40 mins |
| 13 . | CURED @150°C for 20 mins |
| 14 . | CURED @150°C for 60 mins |
| 15 . | CURED@150°C × 40 MINUTES |
| 16 . | CURED@150°C × 40 MINUTES |
| 17 . | CURED@150°C × 40 MINUTES |
| 18 . | CURED@150°C × 40 MINUTES |
| 19 . | CURED@150°C × 40 MINUTES |
| 20 . | CURED@150°C × 40 MINUTES |
| 21 . | CURED@150°C × 40 MINUTES |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier PPHR-1020 | Premier Polymers, LLC. | PP Homopolymer | Premier |
| RABALON® T320C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| Moplen EP300M | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Vistalon™ 2504N | ExxonMobil Chemical | EPDM | Vistalon™ |
| Polifor® 25 CF/20 H NERO | SO.F.TER. SPA | PP Homopolymer | Polifor® |