Durethan® BC 700 HTS DUSXBL 900116
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qgfZi5_DurethanBC700HTSDUSXBL900116.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6-Copolymer, non-reinforced, blow molding, heat-aging stabilized, improved impact strength, improved heat-aging stability |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.03 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 8.1 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 65 | 59 | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 980 | 210 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 28.0 | -- | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 6.5 | -- | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 980 | 230 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% strain, 23°C | 30.0 | 7.00 | MPa | ISO 178/A |
| 23°C 2 | 35.0 | 12.0 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 3(23°C) | 6.1 | 9.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6/66-HI, BHS, 14-010 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.060 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 75 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 110 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 70 | -- | kJ/m² | ISO 180/1A |
| 23°C | 90 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | No Break | -- | ISO 180/1U | |
| 23°C | No Break | No Break | ISO 180/1U | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 50.0 | -- | J | ISO 6603-2 |
| 23°C | 50.0 | -- | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 4100 | -- | N | ISO 6603-2 |
| 23°C | 3300 | -- | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 53.0 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 48.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 212 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 2.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 230 - 280 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive XP11-289A15 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| Karina GRAY PVC COMPOUND 680D18/ 37-CY-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 20/SCF/30 | Lehmann & Voss & Co. | PPA | LUVOCOM® |
| Plenco 03557 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |
| Sylvin 8200-90UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |