Latan 13
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qgciam_Latan-13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyoximethylene (POM). Medium viscosity. Very good tribological properties. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 2.1 to 2.3 | % | |
| Flow : 2.00 mm | 2.0 to 2.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2200 | MPa | |
| 60°C | 1300 | MPa | |
| 90°C | 850 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 55.0 | MPa | |
| Yield, 60°C | 40.0 | MPa | |
| Yield, 90°C | 30.0 | MPa | |
| Break, 23°C | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 10 | % | |
| Break, 23°C | 40 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 5.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact (23°C, 3.20 mm) | 65 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 75.0 | °C | |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 175 to 200 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PC 63 T 15-1M | Plastcom | PP Copolymer | SLOVALEN® |
| Thermoset Plastics 302 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| EMERGE™ PC 4330-10 | Trinseo | PC | EMERGE™ |
| Karina BLACK PVC COMPOUND -E 601D48/ 1-A | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| 3M™ Dyneon™ Perfluoroelastomer PFE E-21464 | 3M Advanced Materials Division | Perfluoroelastomer | 3M™ Dyneon™ Perfluoroelastomer |