A brushable, high-performance, ceramic-filled epoxy for sealing, protecting, and repairing surfaces subject to erosion, corrosion, and wear

Intended Use:

Protect pump casings, impeller blades, gate valves, water boxes, and fan blades; rebuild heat exchangers, tube sheets, and other water circulating equipment; top coat on repaired surfaces; seal and protect new equipment exposed to erosion and corrosion

Product features:

Excellent chemical resistance

Temperature resistance to 350°F

Applies easily with short-bristle brush or roller

Low viscosity, self-leveling liquid

Acceptable for use in meat and poultry plants

NSF® Approved (Certified to ANSI/NSF61)

General Information
Filler / Reinforcement	Ceramic fiber filler
Features	Low viscosity Good chemical resistance
Uses	Repair Materials
Agency Ratings	NSF 61
Appearance	White

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.53	g/cm³
Specific Volume	0.596	cm³/g
Solid content- by Volume	100	%

Additional Information	Nominal Value	Unit	Test Method
Salt Spray	6.8	month
Temperature Resistance - Wet	66	°C
Tensile Shear Adhesion	13.8	MPa	ASTM D1002

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage - Flow	0.20	%	ASTM D2566

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	87		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Flexural Strength	55.2	MPa	ASTM D790
Compressive Strength	105	MPa	ASTM D695

Thermal	Nominal Value	Unit	Test Method
CLTE - Flow	3.4E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value		Test Method
Dielectric Constant	38.7		ASTM D150

Thermoset	Nominal Value	Unit	Test Method
Thermoset Components
Component a	Mixing ratio by weight: 8.5 Mixing ratio by capacity: 5.6
Component B	Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0
Pot Life (24°C)	21	min
Thermoset Mix Viscosity	40000	cP

Additional Information	Nominal Value	Unit	Test Method
Cured 7 days @ 75°F

Uncured Properties	Nominal Value	Unit	Test Method
Curing Time	16	hr

Resin Grade	Manufacturer	Category	Trademark
SILVER® VUL105-W40K/SPTW-55P	Guangdong Silver Age Sci & Tech. Co., Ltd	PVC, Unspecified	SILVER®
Tenite™ Propionate 307A4000018 Clear, Trsp	Eastman Chemical Company	CAP	Tenite™ Propionate
apilon 52® A-6505	API SpA	TPU-Polyester	apilon 52®
LNP™ THERMOCOMP™ SF004S compound	SABIC Innovative Plastics	Nylon 12	LNP™ THERMOCOMP™
OnForce™ LFT LF5200-5017 Grey	PolyOne Corporation	Polyolefin, Unspecified	OnForce™ LFT