Telcar® TL-8451 BLK 940

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	Teknor Apex Company
Trademark:	Telcar®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	qgT8qF_Telcar-TL-8451-BLK-940.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
Telcar TL-8451 BLK 940 is a high performance, halogen-free thermoplastic elastomer designed for electrical applications requireing flexibility over a wide termperture range. Telcar TL-8451 BLK 940 is a high durometer grade that is UV stablized and RoHS compliant. This grade is UL listed and is suitable for both injection molding and extrusion.

General Information
Features	High elasticity High tensile strength Good UV resistance Good heat aging resistance Good flexibility Good coloring Medium liquidity Ozone resistance Good weather resistance Sunlight resistance, 720 hours General Halogen-free Extended tensile rate
Uses	Underground cable Cable sheath Electrical wire sheath material Electrical conductor insulation material Wire and cable applications Wire sheath Industrial cable insulation material Connector cord sheath Terminal cable sheath material
Wire Types	SJEOW
Agency Ratings	UL 1581 .QMTT2.E73402 2
RoHS Compliance	RoHS compliance
UL File Number	QMTT2.E73402
Appearance	Opacity
Forms	Particle
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.998	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	19	g/10 min	ASTM D1238
Carbon Black Content	2.5	%	ASTM D1603

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	82		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Deformation Under Load ¹(150°C)	6.00	%	ASTM D621

Elastomers	Nominal Value	Unit	Test Method
Tensile Strength (Break)	16.5	MPa	ASTM D412
Tensile Elongation (Break)	600	%	ASTM D412

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air (136°C, 168 hr)	110	%	ASTM D573
Change in Ultimate Elongation in Air (136°C, 168 hr)	89	%	ASTM D573
Change in Tensile Strength (60°C, 168 hr, in IRM 902 Oil)	86	%	ASTM D471
Change in Ultimate Elongation (60°C, 168 hr, in IRM 902 Oil)	93	%	ASTM D471

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	105	°C	UL 1581
Brittleness Temperature	< -60.0	°C	ASTM D746
RTI Elec	90.0	°C	UL 746
RTI	90.0	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	38	kV/mm	ASTM D149
Dielectric Constant			ASTM D150
1 kHz	2.10		ASTM D150
1 MHz	2.33		ASTM D150
Dissipation Factor			ASTM D150
1 kHz	2.0E-4		ASTM D150
1 MHz	1.0E-4		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Flame Rating (0.810 mm, All Colors)	HB		UL 94
Oxygen Index	18	%	ASTM D2863

Additional Information
最高连续工作温度，UL-1581：105°C

Injection	Nominal Value	Unit
Rear Temperature	199 - 216	°C
Middle Temperature	213 - 221	°C
Front Temperature	221 - 227	°C
Nozzle Temperature	221 - 229	°C
Processing (Melt) Temp	221 - 229	°C
Mold Temperature	25.0 - 65.6	°C
Injection Pressure	1.38 - 6.89	MPa
Injection Rate	Moderate-Fast
Back Pressure	0.172 - 0.345	MPa
Screw Speed	50 - 100	rpm
Cushion	3.81 - 25.4	mm

Injection instructions
无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	193 - 210	°C
Cylinder Zone 2 Temp.	199 - 216	°C
Cylinder Zone 3 Temp.	213 - 221	°C
Cylinder Zone 5 Temp.	221 - 227	°C
Die Temperature	221 - 229	°C

Extrusion instructions
螺杆转速30 - 100 rpm

Note Message
1 .	Weight 2000 grams

Resin Grade	Manufacturer	Category	Trademark
Polylink Polymer P-11030-GF	Polylink Polymers (India) Ltd.	TPO	Polylink Polymer
DAI-EL™ G-797	DAIKIN AMERICA, INC.	Fluorelastomer	DAI-EL™
Honeywell PCTFE P2000TR	Honeywell	PCTFE	Honeywell PCTFE
Karina IVORY PVC COMPOUND 750-35/1-F-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Plaslube® J-1/30/TF/15 RED	Techmer Engineered Solutions	Nylon 66	Plaslube®