RTP 300 TFE 8 SI 2
| Category: | PC , Polycarbonate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qgLvgg_RTP-300-TFE-8-SI-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2070 | MPa | ASTM D638 |
| Tensile Strength | 48.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 1930 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Compressive Strength | 68.9 | MPa | ASTM D695 |
| Coefficient of Friction (With Metal-Dynamic) | 0.10 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 160 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1300 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 135 | °C | ASTM D648 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.19 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-1 | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 7mil/in.Tensile Elongation, ASTM D-638: 8-10%Wear Factor, K, ASTM D-3702: 50E-10in³/min/ft/lb/hrCoefficient of Friction, Dynamic, ASTM D-3702: 0.10The wear factor and dynamic coefficient of friction were both tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 288 - 343 | °C | |
| Middle Temperature | 288 - 343 | °C | |
| Front Temperature | 288 - 343 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 103 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TP6SKZ (Series: EX/UV) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Akulon® F136-C | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Formolene® L42009M | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| HANWHA CLBA-8450BK | Hanwha Chemical | LLDPE | HANWHA |
| TABOREN® PH 51 G 40 | SILON s.r.o. | PP Homopolymer | TABOREN® |