DOMAMID® A1-001-N1-N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DOMO Engineering Plastics GmbH |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qfSBN1_DOMAMID-A1-001-N1-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, medium viscosity injection moulding grade, Natural |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 165 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 23°C, 72 hr | 0.95 | % | |
| Flow : 23°C, 72 hr | 1.1 | % | |
| Water Absorption 2 | ISO 62 | ||
| Saturation, 23°C | 2.4 | % | |
| Equilibrium, 23°C, 50% RH | 0.30 | % | |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 145 | cm³/g | ISO 307 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 153 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 90.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 4.0 | % | |
| Break | 20 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 156 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 66.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 215 | °C | ISO 306/A50 |
| -- | 199 | °C | ISO 306/B50 |
| Melting Temperature | 221 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | VDE 0303-3 |
| Volume Resistivity | 1.0E+15 | ohms·cm | VDE 0303-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 3(2.00 mm) | 34 | mm/min | ISO 3795 |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | VDE 0471/2 |
| Note Message | |
|---|---|
| 1 . | 50%RH, between 16 to 72 hrs |
| 2 . | 24 hrs |
| 3 . | FMVSS302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 H X 72279 A NATURAL | RTP Company | Nylon 66 | RTP |
| Sinvicomp SFW7525D | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Karina WHITE PVC COMPOUND 837-10/ 37-A-ERYB-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaskon MUF-2A LAR | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |
| LNP™ COLORCOMP™ 144C compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |