Sarlink® TPE ME-2565B XRD
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qeRLDa_Sarlink-TPE-ME-2565B-XRD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink ME-2500 Series are high-flow injection molding materials with excellent UV resistance and adhesion to glass. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 1 sec | 68 | ASTM D2240 | |
| Shaw A, 5 seconds | 65 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Transverse flow : 100% strain, 23°C | 1.80 | MPa | ISO 37 |
| Flow : 100% strain, 23°C | 1.90 | MPa | ISO 37 |
| Tensile Strength | ISO 37 | ||
| Transverse flow : fracture, 23°C | 6.70 | MPa | ISO 37 |
| Flow : fracture, 23°C | 6.20 | MPa | ISO 37 |
| Tensile Elongation | ISO 37 | ||
| Transverse flow : fracture, 23°C | 780 | % | ISO 37 |
| Flow : fracture, 23°C | 740 | % | ISO 37 |
| Tear Strength | ISO 34-1 | ||
| Transverse flow : 23°C | 27 | kN/m | ISO 34-1 |
| Flow : 23°C | 26 | kN/m | ISO 34-1 |
| Compression Set (70°C, 22 hr) | 32 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | ISO 188 | ||
| 110°C, 1008 hr | -1.5 | % | ISO 188 |
| 125°C, 1008 hr | -17 | % | ISO 188 |
| Changes in tensile stress upon fracture in air- Transverse flow | ISO 188 | ||
| 110°C, 1008 hr | -5.0 | % | ISO 188 |
| 125°C, 1008 hr | -8.9 | % | ISO 188 |
| Change in Shore Hardness in Air | ISO 188 | ||
| Support a, 110°C, 1008 hr | 4.0 | ISO 188 | |
| Support a, 125°C, 1008 hr | 6.0 | ISO 188 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 133 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 165 - 175 | °C | |
| Middle Temperature | 175 - 185 | °C | |
| Front Temperature | 187 - 197 | °C | |
| Nozzle Temperature | 187 - 197 | °C | |
| Processing (Melt) Temp | 187 - 197 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 176°F (80°C). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® A3WG7 BK23210 | BASF Corporation | Nylon 66 | Ultramid® |
| Cheng Yu FV3030 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| Daelim Po1y® LH6070S | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Hifax TYC 852X E | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| HiPrene® MT61DT | GS Caltex | PP, Unspecified | HiPrene® |