PRE-ELEC® PS 1326
| Category: | PS Alloy , Polystyrene Alloy |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qcypuR_PRE-ELEC-PS-1326.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PS 1326 is a conductive thermoplastic compound based on polystyrene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PS 1326 has excellent mechanical properties and is easy to injection mould. Typical applications include injection moulded tote bins and carrier tape reels for ESD sensitive products. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.11 | g/cm³ | ASTM D792 |
| -- | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 200°C/21.6 kg | 55 | g/10 min | |
| 200°C/5.0 kg | 1.2 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A | 99 | ||
| Shore D | 73 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 22.8 | MPa | ASTM D638 |
| Yield | 23.0 | MPa | ISO 527-2 |
| -- | 22.8 | MPa | ASTM D638 |
| -- | 23.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break | 80 | % | |
| Flexural Modulus | |||
| 4.00 mm | 1790 | MPa | ASTM D790 |
| 4.00 mm | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | |||
| -20°C | 6.3 | kJ/m² | ASTM D256 |
| -20°C | 7.0 | kJ/m² | ISO 179 |
| 23°C | 9.0 | kJ/m² | ISO 179 |
| 23°C | 8.4 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | |||
| -20°C | 50 | kJ/m² | ASTM D256, ISO 179 |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 4.20 | kJ/m² | |
| 23°C, 4.00 mm | 6.30 | kJ/m² | |
| Notched Izod Impact Strength 3 | ISO 180 | ||
| -20°C | 4.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Unnotched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 44.1 | kJ/m² | |
| 23°C, 4.00 mm | 54.6 | kJ/m² | |
| Unnotched Izod Impact Strength 4 | ISO 180 | ||
| -20°C | 44 | kJ/m² | |
| 23°C | 54 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 77.2 | °C | ASTM D648B |
| 0.45 MPa, Unannealed | 77.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 67.2 | °C | ASTM D648A |
| 1.8 MPa, Unannealed | 67.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 97.2 | °C | ASTM D1525 5 |
| -- | 97.0 | °C | ISO 306/A50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+4 | ohms | IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+3 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 30.0 to 70.0 | °C | |
| Injection Pressure | 75.0 to 120 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 4 mm thickness |
| 4 . | 4 mm thickness |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 1025EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced TPO | POLYTROPE® |
| Stat-Tech™ PC-08CF/000 FR V0 | PolyOne Corporation | PC | Stat-Tech™ |
| VITAMIDE® AR38 | A. Schulman Europe | Nylon 66 | VITAMIDE® |
| LNP™ THERMOCOMP™ YF005 compound | SABIC Innovative Plastics | TPEE | LNP™ THERMOCOMP™ |
| 3M™ Dyneon™ Fluoroelastomer FE 5620Q | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |