LNP™ LUBRICOMP™ HAL23 compound
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qcNFP9_LNP-LUBRICOMP-HAL23-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP HAL23 is a compound based on PA 11 resin containing Aramid Fiber, PTFE. Added features include: Internally Lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 1.1 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 45.0 | MPa | |
| Break | 42.0 | MPa | |
| Tensile Strain (Yield) | 17 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 1900 | MPa | ISO 178 |
| Flexural Stress | 54.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 174 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 72.0 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 8.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.4E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 199 to 210 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 227 to 260 | °C | |
| Mold Temperature | 43.3 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8868-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vital-Line SHM4500 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| ADDILENE J 522 N30 | ADDIPLAST | PP Copolymer | ADDILENE |
| Buna® EP T 5459 CL | LANXESS Corporation | EPDM | Buna® EP |
| Ecomass® 1050TU96 | Ecomass Technologies | Nylon 12 | Ecomass® |