Hanwha Total PE P110PT12
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qcAAf8_Hanwha-Total-PE-P110PT12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| P110PT12 is a high-density polyethylene resin for PEX-A crosslinked pipes. This resin is supplied in powder foam and to be processed by ram-extruder type equipment after mixed with crosslinking agents. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.951 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.021 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 26.5 | MPa | ASTM D638 |
| Fracture | 35.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 500 | % | ASTM D638 |
| Apparent Bending Modulus | 834 | MPa | ASTM D747 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 120 | °C | ASTM D1525 1 |
| Additional Information |
|---|
| Average Particle Size: 140 µHydrostatic Pressure Test, ASTM F876, DIN 16892, 12 MPa, 20°C: >1 hrsHydrostatic Pressure Test, ASTM F876, DIN 16892, 4.56 MPa, 93.3°C: >1000 hrsHydrostatic Pressure Test, ASTM F876, DIN 16892, 4.80 MPa, 95°C: >1 hrsHydrostatic Pressure Test, ASTM F876, DIN 16892, 4.4 MPa, 95°C: >1000 hrsDegree of Crosslink, ASTM F876, DIN 16892: >75 % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 23.0 | °C | |
| Adapter Temperature | 140 - 160 | °C | |
| Die Temperature | 240 - 260 | °C |
| Extrusion instructions |
|---|
| Crossbox Temperature90 to 110 °C |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5405-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen HP2981 | LyondellBasell Industries | PP Homopolymer | Moplen |
| NYLOY® UB-0010N G50N1N | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| GAPEX® RPP20EC10NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| Karina IVORY PVC COMPOUND 750-35/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |