LNP™ THERMOCOMP™ DX13354 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qbsQMO_LNP-THERMOCOMP-DX13354-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Thermocomp* DX13354 compound is a 30% glass fiber reinforced, impact modified PC resin based LDS material solution with stable plating and RF performance. Good surface aesthetics and wide processing window makes it a good candidate for internal and external parts for Laser Direct Structuring applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 280°C/2.16 kg | 10 | g/10 min | |
| 280°C/5.0 kg | 27 | g/10 min | |
| 300°C/1.2 kg | 16 | g/10 min | |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 13.0 | cm³/10min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.050 to 0.10 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8760 | MPa | ASTM D638 |
| -- | 8840 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 120 | MPa | ASTM D638 |
| Break | 120 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 3 | 2.4 | % | ASTM D638 |
| Break | 2.4 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 8020 | MPa | ASTM D790 |
| -- | 8450 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 170 | MPa | ASTM D790 |
| -- | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C 4 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 700 | J/m | ASTM D4812 |
| 23°C 5 | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 126 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 6 | 127 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 122 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 7 | 124 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 6.9E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant | Internal Method | ||
| 1.10 GHz | 3.52 | ||
| 1.90 GHz | 3.44 | ||
| 5.00 GHz | 3.51 | ||
| Dissipation Factor | Internal Method | ||
| 1.10 GHz | 0.014 | ||
| 1.90 GHz | 0.013 | ||
| 5.00 GHz | 0.012 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 270 to 295 | °C | |
| Middle Temperature | 270 to 295 | °C | |
| Front Temperature | 270 to 295 | °C | |
| Nozzle Temperature | 270 to 295 | °C | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 100 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| 7 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ E-185G | Prime Polymer Co., Ltd. | PP Impact Copolymer | Prime Polypro™ |
| NANCAR® 3375 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| Nypol® PA B2 G30 UV BRC0001 NT207 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| FARALLOY® PE-211 | O'Neil Color and Compounding | HDPE | FARALLOY® |
| Formolene FORMAX® L71709H | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene FORMAX® |