SCHULAMID® 612 GF 33 H2
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qbflkO_SCHULAMID612GF33H2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 33% glass fiber reinforced, Polyamide 612 Compound, electrically neutral heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (245°C/5.0 kg) | 32.1 | -- | cm³/10min | ISO 1133 |
| Water Absorption (Saturation, 23°C) | 1.3 | -- | % | ISO 62 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 105 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 8300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 170 | 130 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.0 | 3.6 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1(23°C) | 9000 | -- | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | |||
| 3.5% strain | 250 | -- | MPa | ISO 178 |
| 3.7% strain 3 | 250 | -- | MPa | ISO 178 |
| 3.7% strain, 23°C | 255 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 75 | 65 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 214 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 195 | -- | °C | ISO 75-2/Af |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 240 - 280 | °C | |
| Mold Temperature | 50 - 90 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | at Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 15 FR 4 K1681 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Niuk 70GP20 | Shanghai Niuk New Plastic Technology Co., Ltd. | AS | Niuk |
| ICORENE® 1877 | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |
| OnFlex™ S EH 40A-3S7001 | PolyOne Corporation | TPE | OnFlex™ |
| LNP™ STAT-KON™ MD000ISC compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |