SABIC® PP 83EK10
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qbW1Pg_SABIC-PP-83EK10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This grade combines a very high impact strength, even at low temperatures, with a high stiffness and low flow properties. It is used for extrusion of flat sheets, corrugated board and corrugated pipes. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.2 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 | |
| Shore Hardness (Shore D) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1250 | MPa | ASTM D638 |
| -- | 1250 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 23.0 | MPa | ASTM D638 |
| Yield | 23.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 6.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 10 | kJ/m² | |
| 0°C | 60 | kJ/m² | |
| 23°C | 80 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -20°C | 130 | J/m | ASTM D256A |
| 0°C | No Break | ASTM D256A, ISO 180/1A | |
| 23°C | No Break | ASTM D256A, ISO 180/1A | |
| -20°C | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 85.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 55.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 68.0 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2720 S-30A | RTP Company | SEBS | RTP |
| Shuman PC 930-05V0 | Shuman Plastics, Inc. | PC | Shuman PC |
| WELLAMID Nylon 6000 SUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| KetaSpire® KT-820 SL30 | Solvay Specialty Polymers | PEEK | KetaSpire® |
| Karina NATURAL PVC COMPOUND 800-25/ 1-AYR-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |