Polypropylene - Homopolymer 102-GF02 is a "slightly modified" polypropylene homopolymer with a nominal MFR of 2.0 g/10min, especially designed for the "coextruded biorented film" application using the tenter process. Benefits & Features Improved processability for the production of "coextruded biorented film". Applications Coextruded biorented film using the tenter process. |
General Information | |
---|---|
Features |
|
Uses |
|
RoHS Compliance |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Stress (Yield, 23°C) | 31.0 | MPa | ISO 527-2 |
Flexural Modulus (23°C) | 1350 | MPa | ISO 178 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Peak Melting Temperature 1 | 158 | °C | ASTM D3418 |
Note Message | |
---|---|
1 . | 2nd heating |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Solprene® 1110 | Dynasol Elastomers | SBR, Solution | Solprene® |
TRISTAR® PC-10R | Polymer Technology and Services, LLC | PC | TRISTAR® |
ExxonMobil™ LLDPE LL 5002.09 | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
Elastollan® 1175AW | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
KPOL-NYLON K-NY66/21VCF | KPOL Chem Co. | Nylon 66 | KPOL-NYLON |