DURACON® SX-35
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | DURACON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qaV46Z_DURACON-SX-35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DURACON®SX-35 is a polyoxymethylene (POM) copolymer product,. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Features include:
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 5.60 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 35 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 900 | MPa | ISO 527-2 |
| Tensile Stress | 26.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 25 | % | ISO 527-2 |
| Flexural Modulus | 800 | MPa | ISO 178 |
| Flexural Stress | 32.0 | MPa | ISO 178 |
| Coefficient of Friction | JIS K7218 | ||
| Dynamic 1 | 0.45 | JIS K7218 | |
| With steel-dynamic 2 | 0.52 | JIS K7218 | |
| Wear Factor | JIS K7218 | ||
| 0.49 MPa, 0.30 m/sec 3 | < 1.0 | 10^-8 mm³/N·m | JIS K7218 |
| 0.060 MPa, 0.15 m/sec 4 | 300 | 10^-8 mm³/N·m | JIS K7218 |
| 0.49 MPa, 0.30 m/sec 5 | 600 | 10^-8 mm³/N·m | JIS K7218 |
| 0.060 MPa, 0.15 m/sec 6 | 700 | 10^-8 mm³/N·m | JIS K7218 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 69.0 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | Internal method | ||
| Flow : 23 to 55°C | 1.0E-4 | cm/cm/°C | Internal method |
| Lateral : 23 to 55°C | 1.5E-4 | cm/cm/°C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 9.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 25 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Color Number | CF2001 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 49.0 - 98.0 | MPa | |
| Screw Speed | 100 - 150 | rpm |
| Injection instructions |
|---|
| Injection speed: 5-50 mm/sInjection Holding pressure: Gate sealing time + alphaCooling: Plasticizing time or ejection capable time |
| Note Message | |
|---|---|
| 1 . | vs. M90-44, 0.06 MPa, 15 cm/s |
| 2 . | 0.49 MPa, 30 cm/s |
| 3 . | vs C-Steel, Steel Side |
| 4 . | vs M90-44, M90-44 Side |
| 5 . | vs C-Steel, Material Side |
| 6 . | vs M90-44, Material Side |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 384 HEC | RTP Company | PC | RTP |
| RANPELEN SFI-553 | Lotte Chemical Corporation | PP Terpolymer | RANPELEN |
| Next Nylon 66 Prime Series PG30-01BL | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Dynaprene® SE9050A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Karina WHITE PVC COMPOUND 752D10/152-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |