Comtrex Flexible PVC® 63XCF
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Comtrex Flexible PVC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qaHEM3_Comtrex-Flexible-PVC-63XCF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COMTREX FLEXIBLE PVC 63XCF is a Cadmium Free compound typically used in interior applications such as molding decorative covers for arm rest assemblies that require wear resistance. This compound is available in custom matched black and integral colors. Gloss level will depend on mold design and application. Designed to meet Daimler Chrysler Corporation Material Standard MS-DC526. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation (Break) | 350 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 12.8 | MPa | ASTM D412A |
| Tear Strength 2 | 38.7 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Test Method | |
|---|---|---|---|
| Cold Bend (-29°C, 2.50 cm) | Flexible, No Cracks | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| FMVSS Flammability | Self-Extinguishing (SE) | FMVSS 302 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Weathering Duration 3 | No objectionable change in color or gloss. No objectionable defects. | SAE J1885 | |
| Fog Test | Very Slight Fog | Internal Method | |
| Hot/Cold Cycling - 24 hours | Internal Method | ||
| -29°C | No splitting, cracking, loss of appearance qualities, or physical properties | ||
| 79°C | No splitting, cracking, loss of appearance qualities, or physical properties | ||
| Volatile Loss - 72 hours (79°C) | 0.50 | % | Internal Method |
| Note Message | |
|---|---|
| 1 . | Die C, 500 mm/min |
| 2 . | 50 mm/min |
| 3 . | 600 kJ/m² exposure to Interior Xenon Arc Weather-ometer per SAE J1885. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1387 UP | RTP Company | PPS | RTP |
| Shin-Etsu Elastomer KE-931U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| DOW™ HDPE NG7000 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| Sylvin 3210-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| POCAN® B 5220 XF 000000 | LANXESS GmbH | PBT | POCAN® |