WPP PP PPH5CF3-Black
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qZh2XQ_WPP-PP-PPH5CF3-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Properties shown below for this filled blend are typical for a 33% calcium carbonate filled polypropylene homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 19.0 | MPa | ISO 527-2/5 |
| Flexural Modulus 1 | 2350 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 3.5 | kJ/m² | ISO 179 |
| 23°C | 4.8 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 87.8 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 216 - 221 | °C | |
| Middle Temperature | 216 - 221 | °C | |
| Front Temperature | 218 - 224 | °C | |
| Nozzle Temperature | 224 - 235 | °C | |
| Mold Temperature | 15.6 - 48.9 | °C | |
| Injection Pressure | 4.14 - 7.58 | MPa | |
| Holding Pressure | 1.72 - 4.83 | MPa | |
| Back Pressure | 0.517 - 1.03 | MPa | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| Injection Speed: 1.5 to 2.5 in/sZone 4 Temperature: 435 to 445°FHot Runner Temperature: 435 to 465°FHydraulic Oil Temperature: 110 to 125°FShot Capacity vs. Barrel Capacity: 2.5 to 4Screw Decompression: 0.1 to 0.25 in |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A 38 100 NAT | Radici Plastics | Nylon 66 | Radilon® |
| Sarlink® TPE EE-1290N NAT | Teknor Apex Company | TPE | Sarlink® TPE |
| Sylvin 8348-72UV White 1528 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| 4DUR® 9K22117 FR1 | 4Plas | PBT | 4DUR® |
| Chemraz 592 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |