| RFOO77P is a Halogen Free and Red Phosphorous Free Flame Retardant, Glass Fiber Reinforced, PA66 / PA6 Injection Molding Resin (also known as RF1007Z270EM) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (24 hr) | 0.10 to 0.30 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 10500 | MPa | ISO 178 |
| Flexural Stress | 215 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 60 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 220 | °C | ISO 75-2/Af |
| Ball Pressure Test 4(210°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | |
| 1.50 mm | 775 | °C | |
| 3.00 mm | 825 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 265 to 275 | °C | |
| Front Temperature | 265 to 280 | °C | |
| Processing (Melt) Temp | 270 to 280 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ LLDPE DNDA-8335 NT 7 | The Dow Chemical Company | LLDPE | DOW™ LLDPE |
| NEXUS PC/ABS PC/ABSFR9001 | Nexus Resin Group, LLC. | PC+ABS | NEXUS PC/ABS |
| New-prene™ 6050N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| ISPLEN® PB 181 N2M | REPSOL | PP Impact Copolymer | ISPLEN® |
| LNP™ LUBRICOMP™ Cycoloy_C6303 compound | SABIC Innovative Plastics | PC+ABS | LNP™ LUBRICOMP™ |