VALOX™ V2000DM resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qYxwEB_VALOXV2000DMresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced, directly metallizable PBT injection molding resin with high flow better release characteristics. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 35 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 34.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 2.1 - 2.4 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.080 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.34 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2810 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 59.0 | MPa | ASTM D638 |
| Yield | 59.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 40.0 | MPa | ASTM D638 |
| Fracture | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 20 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/50 |
| Fracture 5 | 100 | % | ASTM D638 |
| Fracture | 15 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2570 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| Flexural Strength 8(Yield, 50.0 mm Span) | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 46 | J/m | ASTM D256 |
| -30°C 10 | 2.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (-30°C) | No Break | ASTM D4812 | |
| Instrumented Dart Impact (23°C, Total Energy) | 54.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 54.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 53.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 185 | °C | ASTM D1525, ISO 306/B120 9 13 |
| -- | 186 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 8.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 232 - 249 | °C | |
| Middle Temperature | 238 - 254 | °C | |
| Front Temperature | 243 - 260 | °C | |
| Nozzle Temperature | 238 - 254 | °C | |
| Processing (Melt) Temp | 243 - 260 | °C | |
| Mold Temperature | 48.9 - 76.7 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Vent Depth | 0.013 - 0.025 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 56M10 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| Starflam AFR450X2 | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| Sylvin 8215-80UV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| XENOY™ X5601WX resin | SABIC Innovative Plastics | PBT+PC+PET | XENOY™ |
| EGYPTENE LL 0220 KJ | Sidpec (Sidi Kerir Petrochemicals Co.) | LLDPE | EGYPTENE |