PBT, non-reinforced, injection moldingExtrusion, improved impact strength

General Information
Features	Impact resistance, good
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Extrusion Injection molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.20	g/cm³	ISO 1183
Apparent Density	0.70	g/cm³	ISO 60
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)	14.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 294-4
Vertical flow direction : 260°C, 2.00mm ¹	1.8	%	ISO 294-4
Vertical flow direction : 120°C, 2 hours, 2.00mm ²	0.40	%	ISO 294-4
Flow direction : 260°C, 2.00mm ³	2.0	%	ISO 294-4
Flow direction : 120°C, 2 hours, 2.00mm ⁴	0.30	%	ISO 294-4
Water Absorption			ISO 62
Saturated, 23°C	0.40	%	ISO 62
Equilibrium, 23°C, 50% RH	0.20	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	70.0	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	1700	MPa	ISO 527-2/1
Tensile Stress (Yield, 23°C)	35.0	MPa	ISO 527-2/50
Tensile Strain (Yield, 23°C)	4.5	%	ISO 527-2/50
Nominal Tensile Strain at Break (23°C)	> 50	%	ISO 527-2/50
Tensile Creep Modulus			ISO 899-1
1 hr	1400	MPa	ISO 899-1
1000 hr	700	MPa	ISO 899-1
Flexural Modulus ⁵(23°C)	1600	MPa	ISO 178/A
Flexural Stress ⁶
3.5% strain	50.0	MPa	ISO 178/A
23°C	55.0	MPa	ISO 178
Flexural Strain at Flexural Strength ⁷(23°C)	6.0	%

Additional Information	Nominal Value		Test Method
Electrolytical Corrosion	A 1		IEC 60426
ISO Shortname	PBT, GHPR, 11-020		ISO 7792

Injection	Nominal Value	Unit	Test Method
Residual Moisture Content	0.0 - 0.020	%	Karl Fisher

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	25	kJ/m²	ISO 179/1eA
23°C	75	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	No Break		ISO 179/1eU
23°C	No Break		ISO 179/1eU
Notched Izod Impact			ISO 180/1A
-30°C	20	kJ/m²	ISO 180/1A
23°C	70	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength			ISO 180/1U
-30°C	No Break		ISO 180/1U
23°C	No Break		ISO 180/1U
Multi-Axial Instrumented Impact Peak Force			ISO 6603-2
-30°C	90.0	N	ISO 6603-2
23°C	110	N	ISO 6603-2

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	90.0	°C	ISO 75-2/B
1.8 MPa, not annealed	55.0	°C	ISO 75-2/A
Vicat Softening Temperature	116	°C	ISO 306/B120
Ball Pressure Test (180°C)	Pass		IEC 60695-10-2
Melting Temperature ⁸	225	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : 23 to 55°C	1.3E-4	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	1.3E-4	cm/cm/°C	ISO 11359-2
Thermal Conductivity (23°C)	0.22	W/m/K	ISO 8302

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093
Volume Resistivity (23°C)	> 1.0E+15	ohms·cm	IEC 60093
Dielectric Strength (23°C, 1.00 mm)	28	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
23°C, 100 Hz	3.20		IEC 60250
23°C, 1 MHz	3.10		IEC 60250
Dissipation Factor			IEC 60250
23°C, 100 Hz	3.0E-3		IEC 60250
23°C, 1 MHz	0.017		IEC 60250
Comparative Tracking Index (Solution A)	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.800 mm	HB		UL 94
1.60 mm	HB		UL 94
Glow Wire Flammability Index (2.00 mm)	650	°C	IEC 60695-2-12
Oxygen Index ⁹	22	%	ISO 4589-2

Injection	Nominal Value	Unit	Test Method
Drying Temperature - Circulation Dryer	120	°C
Drying Time - Circulation Dryer	4.0 - 8.0	hr
Processing (Melt) Temp	250 - 270	°C
Mold Temperature	80.0 - 100	°C

Note Message
1 .	60x60x2; MT 80°C; 600 Bar
2 .	60x60x2
3 .	60x60x2; MT 80°C; 600 Bar
4 .	60x60x2
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	Pull Rate: 2 mm/min; 50% RH
8 .	10°C/min
9 .	Procedure A

Resin Grade	Manufacturer	Category	Trademark
VITAMIDE® BF13BL6262	Jackdaw Polymers	Nylon 6	VITAMIDE®
Nilac MT	Soredi S.p.a.	ABS	Nilac
DOMAMID® 6G20GT96M	DOMO Engineering Plastics SPA	Nylon 6	DOMAMID®
POLYabs F00L	Polykemi AB	ABS	POLYabs
Sylvin 8206-80UV Natural	Sylvin Technologies Incorporated	PVC, Flexible	Sylvin