Chemlon® MDM54
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qYGtkc_Chemlon-MDM54.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MDM54 is an injection molding grade nylon 6 approved by UL. It contains minerals, does not contain halogen and phosphorus, and has a flame retardant grade of V-2. It is mainly used in electrical equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.29 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.90 - 1.6 | -- | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4200 | 1100 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield | -- | 40.0 | MPa | ISO 527-2 |
| Fracture | 77.0 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | 7.0 | % | ISO 527-2 |
| Flexural Modulus | 4000 | 2200 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | |||
| -- 2 | -- | 38.0 | MPa | ISO 178 |
| -- 3 | 110 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 5.5 | 23 | kJ/m² | ISO 179 |
| Notched Izod Impact | 6.0 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 78.0 | 73.0 | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 11 | 9.0 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.90 | 5.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.080 | IEC 60250 | |
| Comparative Tracking Index | > 600 | > 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index | 960 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 24 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 200 | rpm |
| Injection instructions |
|---|
| 背压：低注射压力：高如果材料在空气中暴露的时间不超过3小时，则无需干燥。 |
| Note Message | |
|---|---|
| 1 . | Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5 mm to 4 mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| 2 . | Break |
| 3 . | Yield |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD 4080 | RTP Company | PPA | RTP |
| Double Elephant SX-302 | Suzhou Double Elephant Optical Material Co., LTD. | Acrylic (PMMA) | Double Elephant |
| EnCom GF45 PET UR | EnCom, Inc. | PET | EnCom |
| LEXAN™ 103R resin | SABIC Innovative Plastics | PC | LEXAN™ |
| TECACOMP® PEEK 450 PVX black 9585 | Ensinger GmbH | PEEK | TECACOMP® |