Multi-Flex® TPE A4710 S (H)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Multibase, A Dow Corning Company |
| Trademark: | Multi-Flex® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qXiISa_Multi-Flex-TPE-A4710-S-H-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Multi-Flex® TPE A4710 S (H) is a Thermoplastic Elastomer (TPE) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 50 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 4.60 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 800 | % | ASTM D412 |
| Tear Strength | 20.1 | kN/m | ASTM D624 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 188 | °C | |
| Middle Temperature | 193 | °C | |
| Front Temperature | 199 | °C | |
| Nozzle Temperature | 199 | °C | |
| Processing (Melt) Temp | 199 | °C | |
| Mold Temperature | 26.7 to 43.3 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9610-80 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen RP5058 | PolyMirae | PP Random Copolymer | Moplen |
| Elastollan® WY1157 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| Generic TPO (POE) - Mineral | Generic | TPO (POE) | Generic |
| LNP™ THERMOCOMP™ 9X02841 compound | SABIC Innovative Plastics | PC+PBT | LNP™ THERMOCOMP™ |