Infino GW-1041
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qWrGpS_Infino-GW-1041.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino GW-1041 is a Polycarbonate + ABS (PC+ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: rohs compliant. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 19 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.62 to 0.75 | % | |
| Across Flow : 3.20 mm | 0.67 to 0.82 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1800 | MPa | ASTM D638 |
| -- | 1900 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 50.0 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Break 3 | 59.0 | MPa | ASTM D638 |
| Break | 62.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 110 | % | ASTM D638 |
| Break | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 1800 | MPa | ASTM D790 |
| -- 6 | 2160 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 70.0 | MPa | ASTM D790 |
| -- 8 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 61 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 670 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 540 | J/m | ASTM D256 |
| 23°C 10 | 60 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 126 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 112 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 138 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® PM-9640 (Injection) | Sumitomo Bakelite North America, Inc. | Phenolic | Sumikon® |
| Adiprene® LF 1800A | Chemtura | PUR-Ester/TDI | Adiprene® |
| GLS PP YT29 | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| Latimass 53-04 D009 | LATI S.p.A. | PP Homopolymer | Latimass |
| OxyShield® Plus 1350 | Honeywell | Nylon 6 | OxyShield® Plus |