LNP™ LUBRICOMP™ WL004 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qWpANm_LNPLUBRICOMPWL004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP WL004 is a compound based on Polybutylene Terephalate resin containing PTFE. Added Features; Internally Lubricated Also known as: LNP* LUBRICOMP* Compound WL-4040 Product reorder name: WL004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 18.0 - 21.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow | 1.0 - 1.7 | % | Internal method |
| Transverse flow | 0.80 - 1.7 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 41.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 12 | % | ISO 527-2/5 |
| Flexural Modulus 1 | ISO 178 | ||
| -- | 2200 | MPa | ISO 178 |
| 60°C | 800 | MPa | ISO 178 |
| 100°C | 500 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 68.0 | MPa | ISO 178 |
| 60°C | 21.0 | MPa | ISO 178 |
| 100°C | 14.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.33 | ASTM D3702 Modified | |
| With Self-Static | 0.25 | ASTM D3702 Modified | |
| Flexural Strain at Break 2 | ISO 178 | ||
| -- | 6.0 | % | ISO 178 |
| 60°C | 7.0 | % | ISO 178 |
| 100°C | 7.0 | % | ISO 178 |
| Wear Factor - Washer | 58.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 153 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 60.0 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 - 232 | °C | |
| Middle Temperature | 243 - 254 | °C | |
| Front Temperature | 260 - 271 | °C | |
| Processing (Melt) Temp | 238 - 266 | °C | |
| Mold Temperature | 82.2 - 98.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VYPET VNT 615HP | Lavergne Group | PET | VYPET |
| NORYL™ WCV065 resin | SABIC Innovative Plastics | PPE+Polyolefin | NORYL™ |
| Biograde D-2M | Biograde Group of Companies | Biodeg Polymers | Biograde |
| Hanwha Total PP TB52M | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Sylvin 6169-85 Grey 9290 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |