Biograde® C 9550
| Category: | CA , Cellulose Acetate |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Biograde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qWLZco_Biograde-C-9550.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Biodegradable compound for injection moulding made primarily from renewable resources. Biograde® C 9550 (prev. Biograde® 300 A) |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.67 | g/cm³ | ISO 1183 |
| Apparent Density | 0.94 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 11 - 15 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 7.00 - 10.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 83 | DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4200 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 41.0 | MPa | ISO 527-2 |
| Fracture | 41.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | ISO 527-2 |
| Fracture | 6.5 | % | ISO 527-2 |
| Flexural Modulus | 4050 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 63.0 | MPa | ISO 178 |
| Flexural Strain at Break | 7.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 37 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 118 | °C | ISO 306/A |
| Melting Temperature (DSC) | > 180 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 160 | °C | |
| Middle Temperature | 190 | °C | |
| Front Temperature | 200 | °C | |
| Nozzle Temperature | 205 | °C | |
| Mold Temperature | 30.0 - 75.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Feeding zone: 60°CHolding pressure level: 50 to 80%Melt cushion (of volume): <10%Cooling time: 5smax. Dwell time: 300s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 1530L | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Acculam™ Phenolfab G3 | Accurate Plastics, Inc. | Phenolic | Acculam™ |
| COSMOPLENE® AW864 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| LNP™ LUBRICOMP™ PFP36 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |
| Sylvin 9925-70UV Green 3162 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |