TAROMID B 280 G3 MT5
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qVxDhU_TAROMID-B-280-G3-MT5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6 fibers/mineral 40% reinforced, good dimensional stability combined to good mechanical properties. Available: all colors, heat stabilised (H), UV stabilized (L), with release agent (W). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.25 to 0.40 | % | |
| Across Flow | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.70 | % | ASTM D570, ISO 62 |
| Saturation | 5.5 | % | ASTM D570 |
| Saturation, 23°C | 5.5 | % | ISO 62 |
| Granule Humidity | < 0.10 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7400 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 145 | MPa | ISO 178 |
| Break | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 5.5 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 60 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 190 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50, ASTM D1525 2 |
| Melting Temperature | 222 | °C | ASTM D211, ISO 121 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIGITRON 10020 GF | Ovation Polymers Inc. | PC | RIGITRON |
| TOPAS® 6013S-04 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| Unipren® Elastomers A3 PRTA010 45A EG06S1 UP326 | Petropol Industry and Trade of Polymers LTDA | TPE | Unipren® Elastomers |
| DynaMix™ 4130CF | Polymer Dynamix | PPA | DynaMix™ |
| EMAC® SP2409 | Westlake Chemical Corporation | EMA | EMAC® |