LNP™ THERMOCOMP™ QC008 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qVeBMZ_LNP-THERMOCOMP-QC008-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP QC008 is a compound based on Nylon 6/10 containing 40% Carbon Fiber. Added feature of this grade is: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound QC-1008 Product reorder name: QC008 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.29 | g/cm³ | ASTM D792 |
| -- | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.060 to 0.080 | % | |
| Across Flow : 24 hr | 0.60 to 0.70 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.31 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.31 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 44200 | MPa | ASTM D638 |
| -- | 31900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 233 | MPa | ASTM D638 |
| Yield | 237 | MPa | ISO 527-2/5 |
| Break 3 | 233 | MPa | ASTM D638 |
| Break | 237 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.8 | % | ASTM D638 |
| Yield | 1.6 | % | ISO 527-2/5 |
| Break 5 | 1.8 | % | ASTM D638 |
| Break | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 20300 | MPa | ASTM D790 |
| -- 7 | 22400 | MPa | ISO 178 |
| Flexural Strength 8(Yield, 50.0 mm Span) | 363 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 9 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1300 | J/m | ASTM D4812 |
| 23°C 10 | 68 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 222 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 223 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 217 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 216 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800 B-55A FR A UV | RTP Company | TPO (POE) | RTP |
| RAMSTER PF320G6 | Polyram Ram-On Industries | PBT | RAMSTER |
| Tislamid® PA6 PA6 UNR FR | Tisan | Nylon 6 | Tislamid® PA6 |
| NYCOA Polyamide 4014 HST | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Hifax TYC337P 3 | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |