ASTALOY™ PC/ABS EHA
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qUYvd1_ASTALOY-PC-ABS-EHA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALOY™ PC/ABS EHA is an electroplatable alloy of ABS and Polycarbonate and is designed for injection moulding applications requiring a balance of easy electoplatability, impact toughness, product rigidity, heat resistance and mouldability. Typical applications in the automotive field include electroplated grilles, garnishes and doorhandles. Note: The letters "U" or "W" indicate UV stabilisation has been added [ ie: ASTALOY™ PC/ABS EHAW ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 250°C/3.8 kg | 7.0 | g/10 min | |
| 260°C/5.0 kg | 17 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 51.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 88.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 500 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 45.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 96.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 101 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 106 | °C | |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 5 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 to 100 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 225 to 265 | °C | |
| Middle Temperature | 235 to 275 | °C | |
| Front Temperature | 245 to 285 | °C | |
| Processing (Melt) Temp | 240 to 290 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Rate | Slow | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wanthane® WHT-8285 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | Wanthane® |
| Wondel® S GR0 | Nanjing Julong Engineering Plastics Co., LTD | ABS | Wondel® S |
| Ensinger TECACRYL® | Ensinger Inc. | Acrylic, Unspecified | Ensinger |
| LNP™ LUBRICOMP™ ZL003 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |
| Ultradur® B 4040 G6 HR BK15029 | BASF Corporation | PBT+PET | Ultradur® |