HAIPLEN H30 G4 BA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qUESeV_HAIPLEN-H30-G4-BA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer glass fiber reinforced 20% chemical coupled, good mechanical properties. Available: all colors, UV stabilized (L), heat stabilized (H), laser printable (LP), detergent stabilized(D) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.35 to 0.65 | % | |
| Across Flow | 0.85 to 0.95 | % | |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 50.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 10 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 4500 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 90 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 130 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525, ISO 306/A50 2 1 |
| -- | 135 | °C | ASTM D1525, ISO 306/B50 3 2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech PE SP-1010 | Spartech Plastics | HDPE | Spartech |
| Wellamid® XT1482-BK | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Estane® ZHF 80AT3 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| DINALON® A1S25 G30XV0 | Grupo Repol | Nylon 66 | DINALON® |
| HiFill® POM HO GF25 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | HiFill® |