EMERGE™ PC/ABS 7700 NA
| Category: | PC+ABS , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qSnsyz_EMERGEPCABS7700NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC/ABS 7700 NA Advanced Resin is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. It has superior processability for injection molding applications. This grade has excellent aesthetics, is UV stabilized and is available in custom colors. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.17 | g/cm³ | ASTM D792 |
| -- | 1.18 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 11 | g/10 min | ASTM D1238 |
| 240°C/5.0 kg | 20 | g/10 min | ASTM D1238 |
| 260°C/2.16 kg | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 - 0.60 | % | ASTM D955 |
| Flow | 0.40 - 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.20, injection molding | 2620 | MPa | ASTM D638 |
| 4.00, injection molding | 2560 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield, 3.20mm, injection molding | 60.0 | MPa | ASTM D638 |
| Yield, 4.00mm, injection molding | 55.0 | MPa | ISO 527-2/50 |
| Fracture, 3.20mm, injection molding | 48.3 | MPa | ASTM D638 |
| Fracture, 4.00mm, injection molding | 45.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield, 3.20mm, injection molding | 3.8 | % | ASTM D638 |
| Yield, 4.00mm, injection molding | 3.8 | % | ISO 527-2/50 |
| Fracture, 3.20mm, injection molding | 65 | % | ASTM D638 |
| Fracture, 4.00mm, injection molding | 43 | % | ISO 527-2/50 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2690 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, injection molding | 15 | kJ/m² | ISO 179/1eA |
| 23°C, injection molding | 40 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -18°C, 3.20mm, injection molding | 200 | J/m | ASTM D256 |
| -7°C | 440 | J/m | ASTM D256 |
| 23°C, 3.20mm, injection molding | 480 | J/m | ASTM D256 |
| -30°C, injection molding | 14 | kJ/m² | ISO 180/A |
| 23°C, injection molding | 50 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 90.6 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 88.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 79.4 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 77.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 104 | °C | ASTM D1525, ISO 306/A120 3 1 |
| -- | 94.0 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.2E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 1.60mm, in oil | 26 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 2.86 | IEC 60250 | |
| 1 MHz | 2.80 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 4.0E-3 | IEC 60250 | |
| 1 MHz | 7.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 2 | UL 94 | ||
| 1.5 mm | V-0 | UL 94 | |
| 2.0 mm | 5VB | UL 94 | |
| 2.5 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index 3 | IEC 60695-2-12 | ||
| 1.5 mm | 925 | °C | IEC 60695-2-12 |
| 2.0 mm | 925 | °C | IEC 60695-2-12 |
| 2.5 mm | 925 | °C | IEC 60695-2-12 |
| 3.0 mm | 950 | °C | IEC 60695-2-12 |
| Oxygen Index 4 | 28 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 - 88 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 238 - 274 | °C | |
| Mold Temperature | 60 - 91 | °C |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 压 力1 (10N) |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 3611-80 | Teknor Apex Company | PVC, Flexible | APEX® |
| Dryflex® 502550S | ELASTO | SEBS | Dryflex® |
| HiFill® PP 0114 TC-1 | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| POLYCHIM C 10 BB | POLYCHIM INDUSTRIES | PP Homopolymer | POLYCHIM |
| apigo bio® CM 680 | API SpA | TPO (POE) | apigo bio® |