NORYL™ PCN2910 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qSiIEU_NORYL-PCN2910-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/2.16 kg) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.25 to 0.30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11400 | MPa | ASTM D638 |
| -- | 10600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 123 | MPa | ASTM D638 |
| Yield | 106 | MPa | ISO 527-2/5 |
| Break 3 | 115 | MPa | Internal Method |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | Internal Method |
| Break 5 | 1.5 | % | ASTM D638 |
| Break | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 100 mm Span 6 | 8940 | MPa | ASTM D790 |
| -- 7 | 9130 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 160 | MPa | ISO 178 |
| Yield, 100 mm Span 8 | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.4 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 9(23°C) | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C | 68 | J/m | ASTM D256 |
| 23°C 10 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 330 | J/m | ASTM D4812 |
| 23°C 11 | 14 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 7.10 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 125 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 129 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 140 | °C | ASTM D1525 13 |
| CLTE - Flow (-30 to 30°C) | 2.1E-6 to 3.3E-6 | cm/cm/°C | ASTM E831 |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 65.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 3.00 mm | V-0 | ||
| 2.30 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 260 to 304 | °C | |
| Middle Temperature | 271 to 310 | °C | |
| Front Temperature | 282 to 316 | °C | |
| Nozzle Temperature | 293 to 316 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 76.7 to 104 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 10 mm/min |
| 4 . | Type I, 10 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 2.6 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2.6 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telene® 1650 | Telene S.A.S., a Rimtec Corporation company | DCPD | Telene® |
| SPESIN® KP270HL | Kolon Plastics, Inc. | PBT | SPESIN® |
| WELLAMID Nylon 6000/51 GV 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| NEFTEKHIM PP 8332C (EPD60R) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Polimid B 30 GB | Poliblend S.p.a. | Nylon 6 | Polimid B |