SNOLEN® EP 0.26/51 Y
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | JSC Gazprom neftekhim Salavat |
| Trademark: | SNOLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qSYLqm_SNOLEN-EP-0-26-51-Y.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CHARACTERISTIC PROPERTIES High density polyethylene (HDPE). Extra-high environmental stress crack resistance. High impact strength. High hydrostatic strength for PE 100 grades. UV protection not required. MAJOR APPLICATIONS PE 100 extrusion pipe grades. Process pipes (incl. pressure pipes). Gas pipes. Potable water pipes. Wear plates. Fittings. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.947 to 0.951 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 5.2 to 7.2 | g/10 min | |
| 190°C/5.0 kg | 0.20 to 0.26 | g/10 min | |
| Environmental Stress-Cracking Resistance 1(80°C, 2% Arkopal) | 400 | hr | ISO 16770 |
| Melt Flow Ratio | 25.0 to 31.0 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Resistance to Rapid Crack Propagation, Pc - Test S4 | > 20.0 | bar | ISO 13477 |
| Resistance to Slow Crack Growth - Notch Test (SCG) 2 | > 1000 | hr | ISO 13479 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Resistance to Internal Pressure - Hydrostatic Strength 3(80°C) | > 2 | yr | ISO 1167 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 23.0 | MPa | |
| Break | 36.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 10 | % | |
| Break | > 1000 | % | |
| Flexural Modulus - Secant 4(23°C) | 850 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 74.0 | °C | ISO 306/B50 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | @ 4.0 MPa |
| 2 . | @ 4.6 MPa |
| 3 . | @ 4.6 MPa |
| 4 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene LDPE LD 0304 | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| Boltaron 3015 TruPrint | Boltaron Performance Products | PVC, Rigid | Boltaron |
| Braskem PE EF2126S3 | Braskem | LDPE | Braskem PE |
| Geon™ Vinyl Fittings 216A | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Fittings |
| ESTOPLAST XU 4001GY75 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |