Desmovit® DP R 9920

Category:	TPU-Ester/Ether , Thermoplastic Polyurethane Elastomer (Ester/Ether)
Manufacturer:	geba Kunststoffcompounds GmbH
Trademark:	Desmovit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	qSMb7Z_Desmovit-DP-R-9920.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Ether-based injection molding type with a ratio of 20% glass fiber

Characteristics:

very high stiffness, extreme impact strength and fl exibility at low temperature, very good hydrolysis and microbial resistance, seawater proof, good UV resistance, high shock resistance & high flexibility, good noise absorption, excellent colorability and printability

Applications:

mechanically highly stressed components of technical applications (indoor and outdoor), protectors for skiing, horse riding and motor sports, fishing net sinker, helmets, winter sport products such as ski tips, ski edge protection parts, ski bindings, ski boots, goggles, housings in the offshore area

General Information
Filler / Reinforcement	Glass Fiber, 20% Filler by Weight
Features	Excellent Printability Good Colorability Good Flexibility Good UV Resistance High Impact Resistance High Stiffness Hydrolysis Resistant Low Temperature Flexibility Microbe Resistant Salt Water/Spray Resistant Shock Resistant Sound Damping
Uses	Outdoor Applications Safety Equipment Safety Guards Safety Helmets Sporting Goods
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.30	g/cm³	ISO 1183/A
Molding Shrinkage
Across Flow	0.51	%
Flow	0.12	%

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	67		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress	59.0	MPa	ISO 527-2/200
Tensile Strain (Break)	15	%	ISO 527-2/200
Flexural Modulus ¹			ISO 178
-30°C	3500	MPa
23°C	2000	MPa
Flexural Stress ²			ISO 178
-30°C	131	MPa
23°C	60.0	MPa
Abrasion	78	mm³	ISO 4649

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	20	kJ/m²
23°C	40	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	No Break
23°C	No Break

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	156	°C	ISO 75-2/B
1.8 MPa, Unannealed	119	°C	ISO 75-2/A
Vicat Softening Temperature	94.0	°C	ISO 306/B50
CLTE			DIN 53752
Flow	1.0E-5	cm/cm/°C
Transverse	1.1E-4	cm/cm/°C

Injection	Nominal Value	Unit
Drying Time	2.0	hr
Processing (Melt) Temp	200 to 230	°C
Mold Temperature	40.0 to 80.0	°C

Note Message
1 .	1.0 mm/min
2 .	2.0 mm/min

Resin Grade	Manufacturer	Category	Trademark
EVAL™ SP295	Kuraray Co., Ltd.	EVOH	EVAL™
DOW™ Electrical & Telecommunications DGDK-6862 NT	The Dow Chemical Company	HDPE	DOW™ Electrical & Telecommunications
FORMION® FI 200HFU	A. Schulman Inc.	Ionomer	FORMION®
Hanwha Total PP BI970	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, High Crystal	Hanwha Total PP
LNP™ THERMOCOMP™ GF006 compound	SABIC Innovative Plastics	PSU	LNP™ THERMOCOMP™