Moplen EP300C
| Category: | PP Impact Copolymer , High Melt Strength Polypropylene |
| Manufacturer: | PolyMirae |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qS7DxN_MoplenEP300C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Moplen EP300C is a polypropylene impact copolymer manufactured using the Spheripol process. Potential applications include sheet and profile extrusion, as well as thermoforming. Other specific applications may include food packaging and trays. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 87 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 31.4 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 10 | % | ASTM D638 |
| Flexural Modulus | 1080 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 59 | J/m | ASTM D256 |
| 23°C | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 152 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-15G | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Sylvin 8314-70FUV Natural | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |
| Tool-A-Thane UT-25 | Urethane Tooling & Engineering Corp | PUR, Unspecified | Tool-A-Thane |
| Sylvin 6920X08 White 1490 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sumiliteresin® PR-13349 IP | SBHPP | Phenolic | Sumiliteresin® |