Hostacom G3 R05 105555
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qQyydO_Hostacom-G3-R05-105555.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
"Hostacom" G3 R05 105555 is a 30% glass fiber reinforced PP homopolymer (coupled). It combines excellent stiffness properties with good dimensional stability and low creep under load at elevated temperatures. The grade is available in black color, pellet form. It is not intended for medical, pharmaceutical or drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2554 | ||
| Across Flow | 1.0 to 1.2 | % | |
| Flow | 0.20 to 0.30 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 7000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus - Secant | 6500 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.5 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 150 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 138 | °C | ISO 306/B50 |
| CLTE | DIN 53752 | ||
| Flow : 23 to 80°C | 3.3E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 6.4E-5 | cm/cm/°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARFLON™ GZK3200 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Veroplas K18 | PlastxWorld Inc. | Acrylic (PMMA) | Veroplas |
| VAMPSTAT Y 00U 06 V0 26 SC2 ST | Vamp Tech | Nylon 66 | VAMPSTAT |
| FORMULA P COMP 3220 | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Huafon JF-P-6881 / JF-I-6820 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |