Sumitomo Epoxy E 264H
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Sumitomo Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qQTO4y_Sumitomo-Epoxy-E-264H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| E 264H is a high strength, long fiberglass reinforced epoxy molding compound, which features improved flow in transfer molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.82 | g/cm³ | ASTM D792 |
| Apparent Density | 0.25 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.090 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, Compression Molded) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 94.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 20000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 235 | MPa | ASTM D790 |
| Compressive Strength | 203 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 730 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, Compression Molded | > 282 | °C | |
| 1.8 MPa, Annealed, Compression Molded | > 282 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 17 | kV/mm | |
| -- 3 | 15 | kV/mm | |
| Dielectric Constant 4(1 MHz) | 3.70 | ASTM D2520 | |
| Dissipation Factor 5(1 MHz) | 0.010 | ASTM D150 | |
| Arc Resistance | 125 | sec | ASTM D495 |
| Note Message | |
|---|---|
| 1 . | Dry, 60 Hz |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| 4 . | Wet |
| 5 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-756 | CHI MEI CORPORATION | ABS | POLYLAC® |
| SOLLAMID B 2700 FV 30 | Krisoll Resinas Plásticas Ltda. | Nylon 6 | SOLLAMID |
| Niplene T20 FR V0 | Soredi S.p.a. | PP Homopolymer | Niplene |
| LNP™ THERMOCOMP™ RF0049SP compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Sylvin 8950-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |