| TPC grade with high flexural modulus and high flowing properties |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 80 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 34.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 500 | % | ASTM D638 |
| Flexural Modulus | 520 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (-40°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 203 | °C | ASTM D1525 1 |
| Peak Melting Temperature | 219 | °C | ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C | 1.0E+13 | ohms·cm | |
| 100°C | 1.0E+12 | ohms·cm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 220 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toraypef® 25020 AP1F | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| NYCOA Polyamide 2062 | Nycoa (Nylon Corporation of America) | Nylon 66/6 | NYCOA Polyamide |
| KOPET® KP133G30BL | Kolon Plastics, Inc. | PET | KOPET® |
| SD POLYCA™ FD9082I02 | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |
| ESTOPLAST ZK 8505NN01 | Ester Industries Ltd. | PC+ABS | ESTOPLAST ZK |