Di-Pak™ R-4243
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Di-Pak™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qQ4lus_Di-Pak-R-4243.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
RIGID DI-PAK R-4242/4243 Low cost, fast set potting compounds with excellent properties and FAST TURNOVER. R-4242/4243 are 1:1 by weight or volume, making them ideal for hand pour or automatic metering systems. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 to 1.70 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.15 to 0.30 | % | ASTM D2566 |
| Weight - per cubic inch | 28 | g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | 100 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 15.0 to 19.0 | min | ASTM D2971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1810 | MPa | ASTM D638 |
| Tensile Strength | 34.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.4 | % | ASTM D638 |
| Flexural Strength | 2.05 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 22 | J/m | ASTM D256 |
| Unnotched Izod Impact | 29 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity | 0.37 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 4.00 | ||
| 100 kHz | 3.30 | ||
| Dissipation Factor (25°C, 100 kHz) | 0.019 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Thermoset Mix Viscosity 2(25°C) | 2500 | cP | ASTM D4878 |
| Demold Time (21°C) | 60 to 240 | min |
| Note Message | |
|---|---|
| 1 . | 100 g |
| 2 . | Range: 2000 to 3000 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 103 HS | RTP Company | PP, Unspecified | RTP |
| X-Pro PP 4218 | CTC Plastics, LLC | PP Copolymer | X-Pro |
| Sarlink® TPE ML-1640N NAT (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| 3M™ Dyneon™ PTFE Compound PDR 05017 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| KOPA® KN133G20HIBK | Kolon Plastics, Inc. | Nylon 6 | KOPA® |