PRIME TPO E-2910
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | PRIME TPO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qOclxx_PRIME-TPO-E-2910.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRIME TPO E-2910 is a Polypropylene Random Copolymer (PP Random Copolymer) product. It is available in Asia Pacific, Europe, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.8 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 17.0 | MPa | |
| Break | 22.0 | MPa | |
| Tensile Strain (Break) | < 500 | % | ISO 527-2 |
| Flexural Modulus | 430 | MPa | ISO 178 |
| Flexural Stress | 17.0 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 80 | µm | |
| Tensile Modulus | JIS Z1702 | ||
| MD : 80 µm | 430 | MPa | |
| TD : 80 µm | 430 | MPa | |
| Tensile Stress | JIS Z1702 | ||
| MD : Break, 80 µm | 39.0 | MPa | |
| TD : Break, 80 µm | 39.0 | MPa | |
| Tensile Elongation | JIS Z1702 | ||
| MD : Break, 80 µm | < 500 | % | |
| TD : Break, 80 µm | < 500 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 15 | kJ/m² | ISO 180 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | JIS K7105 | ||
| 80.0 µm 1 | 0.60 | % | |
| 80.0 µm 2 | 9.0 | % |
| Note Message | |
|---|---|
| 1 . | Internal |
| 2 . | All |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ C24UST5L | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| VECTRA® FIT30 | Celanese Corporation | LCP | VECTRA® |
| HiFill® PBT GB40 | Techmer Engineered Solutions | PBT | HiFill® |
| POLYFORT® FPP 20 GFC LE K1400 | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| ESTOPLAST XU 6430NGY144 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |