| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qNo2xY_LNPTHERMOCOMPPF00DSBK1G298compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* PF00DS is a compound based on PA6 resin containing Glass Fiber. Added features of this material include: Heat Stabilized. Custom color Black. Also known as: LNP* THERMOCOMP* Compound PF10013HS Product reorder name: PF00DS-BK1G298 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 - 0.20 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 235 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 19000 | MPa | ISO 178 |
| Flexural Stress | 335 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 65 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 100 mm Span) | 220 | °C | ISO 75-2/Ae |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 249 - 260 | °C | |
| Middle Temperature | 266 - 277 | °C | |
| Front Temperature | 277 - 288 | °C | |
| Processing (Melt) Temp | 266 - 277 | °C | |
| Mold Temperature | 82 - 93 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNISOFT TPE™ ST-93A-CL-1-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| NEXT REPROCESSED PC/ABS 830-300R | NEXT Specialty Resins, Inc. | PC+ABS | NEXT REPROCESSED |
| Jackdaw ABS/PC FX10BK6455 | Jackdaw Polymers | PC+ABS | Jackdaw ABS/PC |
| K-Bin Rigid PVC KB-5001 | K-Bin, Inc. | PVC, Rigid | K-Bin Rigid PVC |
| Plaslube® PA6 GF20 RM L BK | Techmer Engineered Solutions | Nylon 6 | Plaslube® |