Ferro PP LPP30BC56WH
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qMzzIT_Ferro-PP-LPP30BC56WH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ferro PP LPP30BC56WH is a Polypropylene Homopolymer (PP Homopolymer) material filled with 30% calcium carbonate. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Ferro PP LPP30BC56WH: Homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.5 | % | |
| Across Flow | 1.6 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 73 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2070 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 24.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 25 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : 23°C | 1980 | MPa | |
| Tangent : 23°C | 2280 | MPa | |
| Flexural Strength (23°C) | 37.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 690 | J/m | ASTM D4812 |
| Gardner Impact (23°C) | 2.82 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 116 | °C | |
| 1.8 MPa, Unannealed | 62.8 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 202 to 204 | °C | |
| Middle Temperature | 204 to 210 | °C | |
| Front Temperature | 210 to 213 | °C | |
| Nozzle Temperature | 213 to 218 | °C | |
| Mold Temperature | 43.3 to 51.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V937 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Alathon® M6020 | LyondellBasell Industries | HDPE, MMW | Alathon® |
| Diakon® TD735 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| ELASTOSIL® R 750/40 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Estane® 58137 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |