Ingeo™ 4044D
| Category: | PLA , Polylactic Acid |
| Manufacturer: | NatureWorks® LLC |
| Trademark: | Ingeo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qMOqVr_Ingeo-4044D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ingeo 4044D is a NatureWorks LLC production grade that is formulated to meet the needs of reactive extrusion processes. When extruded with epoxy functional additives such as BASF Joncryl® ADR 4368C, this grade reacts and chain extends / branches consistently resulting in higher shear viscosity and improved melt strength. Typical addition rates of Joncryl® materials are less than 0.5% by weight. Consultation with your NatureWorks technical representative is recommended before embarking on any reactive extrusion program with this grade. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ASTM D1505 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Carbon Dioxide Transmission Rate (25 µm) | 2850 | cm³/m²/24 hr | Internal method |
| Oxygen Transmission Rate (25 µm) | 680 | cm³/m²/24 hr | ASTM D1434 |
| Water Vapor Transmission Rate (25 µm) | 380 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 145 - 160 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°) | 90 | ASTM D1003 | |
| Haze | 2.1 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | < 0.025 | % | |
| Hopper Temperature | 45.0 | °C | |
| Cylinder Zone 1 Temp. | 179 | °C | |
| Cylinder Zone 2 Temp. | 191 | °C | |
| Cylinder Zone 3 Temp. | 199 | °C | |
| Adapter Temperature | 199 | °C | |
| Melt Temperature | 202 - 218 | °C | |
| Die Temperature | 199 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 20-100 rpmL/D ratios from 24:1 to 30:1Compression ratio of 2.5:1 to 3:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RxLOY™ FFS-NPP00NP03NA | Ferro Corporation | PP Alloy | RxLOY™ |
| Safron® H511-03 | Safripol (PTY) LTD | PP Homopolymer | Safron® |
| NORYL™ GFN2 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| LEXAN™ HFD4271 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Karina GOLDY MB (SP31471) -E 45/ 28-GEN | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |